Welcome to our site! EDAboard.com is an international Electronics Discussion Forum focused on EDA software, circuits, schematics, books, theory, papers, asic, pld, 8051, DSP, Network, RF, Analog Design, PCB, Service Manuals... and a whole lot more! To participate you need to register. Registration is free. Click here to register now.
II-VI compounds are not necessarily insulating, but
those oxides are also not necessarily semiconductors
(or II-VI).
I would suggest digging into II-VI semiconductor texts,
material manufacturers' support docs, and see if you
can find any discussion groups that are into that niche.
It's less popular than III-V, mostly people doing electro-
optical stuff (thin film solar, infrared imaging, etc.).